Strenx® 700MC Plus
Loading component...
Dimension Range
Strenx® 700 MC Plus is available as cut to length sheets in thicknesses of 3.0 - 12.0 mm, widths up to 1525 mm and lengths up to 12300.
Mechanical Properties
(mminches)
(mminches)
(min MPaksi)
(MPaksi)
(min %)
(mminches)
(mminches)
(min MPaksi)
(MPaksi)
(min %)
1) If ReH is not applicable then Rp0.2 is used. On thicknesses >8 mm the minimum yield strength may be 20MPa lower.
2) For both longitudinal and transverse direction.
The mechanical properties are tested in the longitudinal direction.
Impact Properties
Charpy V 10x10 mm test specimen 1)
1) Impact testing in the transverse direction is available if specified at the time of order. Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 5mm. The specified minimum value corresponds to a full-size specimen.
Chemical Composition (heat analysis)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
1) Sum of Nb, V and Ti = max 0.22%.
The steel is grain refined.
Carbon Equivalent CET(CEV)
Thickness
Tolerances according to Strenx® Thickness Guarantees. Strenx® Guarantees offer considerably narrower thickness tolerances compared to EN 10 051.
Length and Width
Width and length tolerances according to SSAB standard. The SSAB standard offer narrower width and length tolerances compared to EN 10 051. Length tolerances only applyfor cut to length sheets
Shape
Tolerances according to EN 10 051. Narrower tolerances according to the SSAB standard are available on request.
Flatness
Tolerances according to Strenx® Flatness Guarantees Class A. Strenx® Flatness Guarantees offer narrower tolerances compared to EN 10 051. Flatness guarantees only applyfor cut to length sheets.
Surface Properties
Delivery Conditions
Thermomechanically Rolled. Strenx® 700 MC Plus is available in as rolled or pickled surface condition.
Fabrication and Other Recommendations
Welding, bending and machining
Strenx® 700 MC Plus has good welding, cold forming and cutting performance.
Strenx® 700 MC Plus is a cold forming steel not suited for heat treatments at temperatures above 580°C since the material then maylose its guaranteed properties.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support, [email protected]. Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the product.